¿Qué es la galvanoplastia de aleación de plomo y estaño?

Lead-tin alloy plating is widely used in industry. By changing the concentration ratio of two metal ions in the plating solution, various lead-tin alloys with different lead and tin contents can be obtained. Alloys containing 6% to 10% tin in the coating are plated on steel strips to improve corrosion resistance, solderability and adhesion to paint, and have good lubricating properties; coatings containing 15% to 25% tin are commonly used in Surface lubrication, adhesion and soldering; alloy coating containing 45% to 55% tin can be used to prevent corrosion of seawater and other media; coating containing 55% to 65% tin can improve the solderability of the surface of electronic components. Adding 1% to 3% of lead to pure tin can prevent the formation of "tin whiskers". The content of tin in the lead-tin alloy coating increases with the increase of tin content and current density in the bath.

1) El revestimiento de aleación con fracción de masa de estaño de 5% a 15% tiene un buen rendimiento anticorrosivo y lubricante, y se usa a menudo para la anticorrosión de productos de acero.

2) The alloy coating with a mass fraction of 6% to 20% of tin has excellent wear-reducing performance and is often used for electroplating on the surface of sliding bearings.

3) El revestimiento de aleación con una fracción de masa de 60 % a 65 % de estaño tiene una excelente resistencia a la corrosión y soldabilidad, y a menudo se usa para la galvanoplastia de placas de circuito impreso.

4) El recubrimiento de aleación con fracción de masa de estaño de 75% a 90% tiene buena soldabilidad y se usa a menudo en la galvanoplastia de cables de componentes electrónicos.

5) Si se agrega de 1% a 3% de plomo al estañado puro, puede prevenir de manera efectiva la formación de filamentos de estaño.